Synthetic Calcium Aluminate Slags
Keywords
synthetic calcium aluminate slags, premelted refining slags, calcium aluminate, premelted calcium aluminate, flux
Introduction
At present, most steel plants in the world generally adopt Ladle refining, to reduce gas inclusion and make molten stell evenly, in order to realize high yield, high quality and low cost steel making. So Synthetic Calcium Aluminate Slags is designed and manufactured to meet the above requirement and take a very important role in steel refining.
Properties
Low molten point, fast molten, shorten refining time and energy consuming.
Good fuidity, desulphurization and inclusion reducing
No flame, little dust emission and good safety in use
No water absorption and no metamorphosing
Effectual submerged arc, and reduce electric arc to burn and erode ladle lining, and enhance ladle life.
Specification
1. CaO: 49 - 54% Al2O3: 41 - 45% SiO2: 3.8% max. TiO2: 2.8% max. Fe2O3: 1.8% max. MgO: 2.0% max.
2. CAO : 53% - 56% , AL2O3 : 32% - 37% , SIO2 : 4%MAX , FE2O3 : 1.5% MAX , MGO : 3% MAX , P : 0.05% MAX , S : 0.1% MAX
3. Al2O3 39 - 43% CaO 32 - 36% SiO2 5.5% max Fe2O3 3% max TiO2: 4% max MgO: 11 - 15%
4. CaO: 47-53%, Al2O3: 43-49%, TiO2: 0.05% max, Fe2O3: 0.15% max, SiO2: 1% max, MgO: 0.2% max, S: 0.08 max
5. CaO 48-53 %, Al2O3 38-43 %, SiO2 3.5 %MAX, TiO2 2 % MAX, Fe2O3 1.2 % MAX
6. MgO 10,5 % min, CaO 22,0 % min. Al2O3 49,5 % min. SiO2 7,0 % max. Fe2O3 3,5 % max.
TiO2 4,0 % max.
7. CaO 33% Min. Al2O3 50-55% SiO2 6.0% Max. TiO2 4.0% Max. MgO 2.0% Max.Fe2O3 2.5% Max.
8. CaO : 47-56%, Al2O3 : 35-44%, SiO2: 5% max. Fe2O3: 2.0% max. P: 0.15% max, S: 0.15% max
9. MgO:11.0% min, CaO:32 % min, Al2O3:39% min, SiO2 : 5.5% max, Fe2O3:3.0% max, TiO2 : 4.0% max
10. CaO: 45 - 52%, Al2O3: 33-40%, MgO: 8-15%, SiO2: 3% max, S: 0.1% max, P: 0.05% max, TiO2: 0.06% max
Size: 0-30 mm
Melting point: 1350 C max
Principal mineralogical phase: C12A7
CAS No.: 65997-16-2 or 12042-68-1
Other specification can be manufactured according to customers requirement.
Application Method
Adding Calcium Aluminate in the furnace. Dosage: one ton molten steel needs Calcium Aluminate around 2-10 kg, and density of molten steel is greater than Calcium Aluminate. Then, argon gas is pumped in from the bottom of furnace, it drives the calcium aluminate to mix with the molten steel completely. Meanwhile, the molten Calcium aluminate adsorbs sulphur substance. Finally, dregs will suspend on the surface of molten steel due to it’s low density and can also keep warmness.
Application Functions
Desulphurization
Deoxygenation
Impurities absorption
Ladle lining protection
Packing
1200KG, 1000KG per sack
|
|
|
|
|
|
|
| Posted by |
Randall Liu
|
| e-Mail | Contact company |
Company
| Henan Kingway Chemicals Co., Ltd.
| | Address | B908, Xingye Mansion, 22 Nongye RD | City & ZIP
| Zhengzhou & 450008
| Country
| China 
| Phone
| For registered Members only.
| Fax
| For registered Members only.
| | Key Customers / Clientele | Calcium Aluminate & CAC, HAC, refractory | | Company Profile | Henan Kingway Chemicals Co., Ltd. was set up under the approval of Ministry of Foreign Trade and Economic Cooperation (China) in 2001 and lies in Zhengzhou, China. Our Co. mainly deals with chemicals, mineral products, textiles, and light industrial products such as aluminate cement, calcium aluminate etc. The registered capital is USD 3.50 million and annual turnover is more than USD 10 million (in 2005). We have established good business relations with more than 30 countries & areas. Our company aims to exploit the aluminate cement and calcium aluminate market all over the world now. Warmly welcome establishing business relations with us!
(randall@hnkingway.com)Good international business reputation makes our business become more prosperous every day. We will be with lower product price, higher product quality, reliable business reputation and considerate after-sale service for serving you wholeheartedly.
| | URL | For registered Members only. | | Rating |  (0 reviews) | | Popular tags | | |
| |
|
 | | Keywords (seperated by comma) | synthetic calcium aluminate slags | | Product Specifications | 1. CaO: 49 - 54% Al2O3: 41 - 45% SiO2: 3.8% max. TiO2: 2.8% max. Fe2O3: 1.8% max. MgO: 2.0% max.
2. CAO : 53% - 56% , AL2O3 : 32% - 37% , SIO2 : 4%MAX , FE2O3 : 1.5% MAX , MGO : 3% MAX , P : 0.05% MAX , S : 0.1% MAX
3. Al2O3 39 - 43% CaO 32 - 36% SiO2 5.5% max Fe2O3 3% max TiO2: 4% max MgO: 11 - 15%
4. CaO: 47-53%, Al2O3: 43-49%, TiO2: 0.05% max, Fe2O3: 0.15% max, SiO2: 1% max, MgO: 0.2% max, S: 0.08 max
5. CaO 48-53 %, Al2O3 38-43 %, SiO2 3.5 %MAX, TiO2 2 % MAX, Fe2O3 1.2 % MAX
6. MgO 10,5 % min, CaO 22,0 % min. Al2O3 49,5 % min. SiO2 7,0 % max. Fe2O3 3,5 % max.
TiO2 4,0 % max.
7. CaO 33% Min. Al2O3 50-55% SiO2 6.0% Max. TiO2 4.0% Max. MgO 2.0% Max.Fe2O3 2.5% Max.
8. CaO : 47-56%, Al2O3 : 35-44%, SiO2: 5% max. Fe2O3: 2.0% max. P: 0.15% max, S: 0.15% max
9. MgO:11.0% min, CaO:32 % min, Al2O3:39% min, SiO2 : 5.5% max, Fe2O3:3.0% max, TiO2 : 4.0% max
10. CaO: 45 - 52%, Al2O3: 33-40%, MgO: 8-15%, SiO2: 3% max, S: 0.1% max, P: 0.05% max, TiO2: 0.06% max
Size: 0-30 mm
Melting point: 1350 C max
Principal mineralogical phase: C12A7
CAS No.: 65997-16-2 or 12042-68-1
Other specification can be manufactured according to customers requirement.
| | Industry Category | 3824 | | Quality/Safety Certifications | ISO9000 | | Delivery Lead Time | 20 days | | Payment & Price Terms | L/C | | My Offers | Synthetic Calcium Aluminate Slags
Keywords
synthetic calcium aluminate slags, premelted refining slags, calcium aluminate, premelted calcium aluminate, flux
Introduction
At present, most steel plants in the world generally adopt Ladle refining, to reduce gas inclusion and make molten stell evenly, in order to realize high yield, high quality and low cost steel making. So Synthetic Calcium Aluminate Slags is designed and manufactured to meet the above requirement and take a very important role in steel refining.
Properties
Low molten point, fast molten, shorten refining time and energy consuming.
Good fuidity, desulphurization and inclusion reducing
No flame, little dust emission and good safety in use
No water absorption and no metamorphosing
Effectual submerged arc, and reduce electric arc to burn and erode ladle lining, and enhance ladle life.
Specification
1. CaO: 49 - 54% Al2O3: 41 - 45% SiO2: 3.8% max. TiO2: 2.8% max. Fe2O3: 1.8% max. MgO: 2.0% max.
2. CAO : 53% - 56% , AL2O3 : 32% - 37% , SIO2 : 4%MAX , FE2O3 : 1.5% MAX , MGO : 3% MAX , P : 0.05% MAX , S : 0.1% MAX
3. Al2O3 39 - 43% CaO 32 - 36% SiO2 5.5% max Fe2O3 3% max TiO2: 4% max MgO: 11 - 15%
4. CaO: 47-53%, Al2O3: 43-49%, TiO2: 0.05% max, Fe2O3: 0.15% max, SiO2: 1% max, MgO: 0.2% max, S: 0.08 max
5. CaO 48-53 %, Al2O3 38-43 %, SiO2 3.5 %MAX, TiO2 2 % MAX, Fe2O3 1.2 % MAX
6. MgO 10,5 % min, CaO 22,0 % min. Al2O3 49,5 % min. SiO2 7,0 % max. Fe2O3 3,5 % max.
TiO2 4,0 % max.
7. CaO 33% Min. Al2O3 50-55% SiO2 6.0% Max. TiO2 4.0% Max. MgO 2.0% Max.Fe2O3 2.5% Max.
8. CaO : 47-56%, Al2O3 : 35-44%, SiO2: 5% max. Fe2O3: 2.0% max. P: 0.15% max, S: 0.15% max
9. MgO:11.0% min, CaO:32 % min, Al2O3:39% min, SiO2 : 5.5% max, Fe2O3:3.0% max, TiO2 : 4.0% max
10. CaO: 45 - 52%, Al2O3: 33-40%, MgO: 8-15%, SiO2: 3% max, S: 0.1% max, P: 0.05% max, TiO2: 0.06% max
Size: 0-30 mm
Melting point: 1350 C max
Principal mineralogical phase: C12A7
CAS No.: 65997-16-2 or 12042-68-1
Other specification can be manufactured according to customers requirement.
Application Method
Adding Calcium Aluminate in the furnace. Dosage: one ton molten steel needs Calcium Aluminate around 2-10 kg, and density of molten steel is greater than Calcium Aluminate. Then, argon gas is pumped in from the bottom of furnace, it drives the calcium aluminate to mix with the molten steel completely. Meanwhile, the molten Calcium aluminate adsorbs sulphur substance. Finally, dregs will suspend on the surface of molten steel due to it?s low density and can also keep warmness.
Application Functions
Desulphurization
Deoxygenation
Impurities absorption
Ladle lining protection
Packing
1200KG, 1000KG per sack
| | Product Portfolio / Other Products | Amorphous Calcium Aluminate
Keywords
amorphous calcium aluminate, non crystalline calcium aluminate, non crystallized calcium aluminate, amorphous C12A7, ACA, concrete accelerator, CAS No. 12042-68-1, cement addititve, shotcrete additive, concrete additives
Description
ACA are the white-green grains and balls. Generally, the grains are ground into fine powder, the ACA powder and OPC (ordinary portland cement) are formulate into Rapid-hardening Mortar and Self-leveling mortar etc. With good performance of rapid strength and little dry shrinkage.
It is a special raw material for concrete and cement.
It can make the rapid setting time, good strength in concrete and cement. It is mainly used in shotcrete, concrete ground hardening and rapid setting etc.
CAS No. 12042-68-1
Specification
(CaO 42 min)( Al2O3 38-42)( SiO2 3-5)( TiO2 3.0)( Fe2O3 3.0) %
(CaO 46-49)( Al2O3 42 min)( SiO2 5 max)( TiO2 1.0 max)( Fe2O3 1.0 max) (MgO 1 max) %
Size: 0-50mm
Other chemical composition can be produced according to customers' requirement.
Application
Shotcrete
Concrete accelerator
Rapid setting, rapid hardening cement
Concrete ground harding
Rapid-hardening Mortar and Self-leveling mortar etc.
Packing
1000 KG per bag
| | Customers | steel plants and concrete suppliers | | Detailed Company Introduction | Henan Kingway Chemicals Co., Ltd. was set up under the approval of Ministry of Foreign Trade and Economic Cooperation (China) in 2001 and lies in Zhengzhou, China. In 2006, we obtain ISO9001: 2000 System Manage Certificate. Our Co. mainly deals with Concrete admixtures, amorphous calcium aluminate, superplasticizers, Refractories, Calcium aluminate cement, Calcium aluminate for metallurgy etc. The registered capital is USD 3.50 million and annual turnover is more than USD 10 million in 2005.
Good international business reputation makes our business become more prosperous every day. We will be with lower product price, higher product quality, reliable business reputation and considerate after-sale service for serving you wholeheartedly.
Main product: superplasticizer, amorphous calcium aluminate, polycarboxylate, naphthalene sulfonate, formaldehyde condensate, melamine sulfonate, sodium gluconate, sodium lignosulfonate, refractories, calcium aluminate cement, CSA cement
Products list:
1. Concrete Admixtures, superplasticizers, amorphous calcium aluminate
2. Calcium Aluminate for steel making, synthetic slag
3. Monolithic refractory materials for metallurgy
4. Refractory Bricks and other refractory tools for metallurgy
5. Calcium Alumiante Cements
6. Calcium sulphoaluminate cements (CSA cement related)
| | FOB Price & Port | USD50 million | | Packaging Details | 20 | | Our Team | Mr. Randall LIU | | Web Site | For registered Members only. |
|
|
|
|
|
| Product Details |
| Product id |
258792 |
| Visits |
208 |
| Date |
2010.08.02 |
|
|
|  |
|
|
Trademetro.net Trade Leads / Minerals, Metals & Materials / Non-metallic Materials
Company Profile
Contact
TradeMetro.net Member Login