Iron Oxide

Iron Oxide yellow

Type

Fe2O3 (%)

Oil absorption (ml/100g)

Res. on 325 mesh (%)

Water sol. Salts (%)

Moisture (%)

PH value

Tamped apparent density (g/cm3)

Particle shape

ΔE compared with std.

Tinting strength (%)

311

≥86 

25~35 

≤0.3 

≤0.3 

≤1.0 

3~7 

0.4-0.6 

Acicular 

≤1 

95~105 

313

≥86 

25~35 

≤0.3 

≤0.3 

≤1.0 

3~7 

0.3-0.5 

Acicular 

≤1 

95~105 

586

≥86 

25~35 

≤0.3 

≤0.3 

≤1.0 

3~7 

0.4-0.6 

Acicular 

≤1 

95~105 

587

≥85 

25~35 

≤0.5 

≤0.3 

≤1.0 

3~7 

0.3-0.5 

Acicular 

≤1 

95~105 

420

≥86 

25~35 

≤0.5 

≤0.3 

≤1.0 

3~7 

0.3-0.5 

Acicular 

≤1 

95~105 

Iron Oxide red

Type

Fe2O3 (%)

Oil absorption (ml/100g)

Res. on 325 mesh (%)

Water sol. Salts (%)

Moisture (%)

PH value

Tamped apparent density (g/cm3)

Particle shape

ΔE compared with std.

Tinting strength (%)

Y101

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.7-1.1

Spherical

≤1

95~105

110

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.7-1.1

Spherical

≤1

95~105

120

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.7-1.1

Spherical

≤1

95~105

130

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.7-1.1

Spherical

≤1

95~105

230

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.8-1.2

Spherical

≤1

95~105

140

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

0.9-1.3

Spherical

≤1

95~105

160

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

1.0~1.4

Spherical

≤1

95~105

180

≥96

15~25

≤0.3

≤0.3

≤1.0

3~7

1.3-1.7

Spherical

≤1

95~105

190

≥95

15~25

≤0.5

≤0.5

≤1.0

3~7

0.7-1.1

Spherical

≤1

95~105